• Model NO.：W262
• Dimension：Diameter≥8.3mm, Length≤700mm
• Surface：Swaged State
• Transport Package：Wooden Box for Plywood-Double Layer
• Specification：92~95%, W-Ni-Fe
• Origin：Mudanjiang
• HS Code：8101999000

Basic Info.

Model NO. W262 Dimension Diameter≥8.3mm, Length≤700mm Surface Swaged State Transport Package Wooden Box for Plywood-Double Layer Specification 92~95%, W-Ni-Fe Origin Mudanjiang HS Code 8101999000

Product Description

Introduction of Tungsten Alloy swaged rod

The normal tungsten alloy rod after swaging, ultimate tensile strength and hardness would be increased greatly. The ultimate tensile strength of general tungsten alloy rod is 920 MPa, hardness is 25HRC. However, after swaging, the ultimate tensile strength can reach 1200 MPa, hardness is 35HRC. We could even control at 1400 MPa, 40HRC. This type of rod is one of our main products. Usually the composition of this kind of products is 92%WNiFe.

1. Dimension: Diameter≥8.3mm, Length≤700mm

2. Density: 17.0-18.10 g/cm3
3. Composition: W content: 92~95%, W-Ni-Fe
4. Surface: swaged state

 

Tungsten Alloy Military Swaging Rod Main Properties:

* High density 
* High melting point 
* Small volume 
* Excellent hardness 
* Superior wearing resistance 
* High ultimate tensile strength 
* High ductility 
* High temperature resistance 
* Low vapor pressure

 

Appliance of tungsten heavy alloy swaged rod

Tungsten alloy swaging rod can be use in machining, CNC toolings, anti-seismic mill holder etc.

 

Grade	State	Density (g/cc)	UST	Elongation (%)	Hardness (HRC)	Impact toughness (MJ/m2)	Yield strength (MPa)
W263	Swaging	17.25±0.15	≥1450	≥8	≥35	≥0.3	≥1350
W262	Swaging	17.50±0.15	≥1450	≥5	≥35	≥0.3	≥1350
W261	Swaging	17.60±0.15	≥1050	≥6	≥35	≥0.3	≥900
W253	Swaging	17.40±0.15	≥1450	≥8	≥35	≥0.3	≥1375
W243	Swaging	17.60±0.15	≥1450	≥7	≥35	≥0.3	≥1375
W232	Swaging	18.10±0.15	≥1400	≥6	≥37	≥0.1	≥1350
W231	Swaging	18.30±0.15	≥1050	≥3	≥37	≥0.1	≥800
W221	Swaging	18.50±0.15	≥1350	≥2	≥37	≥0.07	≥1250